THE RESULT ON THE TABLE IS WEIGHT OF BREAKING POINT.
P.541
| FIBER PROTECTOR TEST RESULTS |
| 1.TENSILE STRENGTH TEST | 2.COMPRESSION BREAKING LOAD TEST | 3.BEND-BREAKING LOAD TEST | 4.TEST CERTIFICATE |
3.BEND-BREAKING LOAD TEST
| METHOD OF TEST | PURPOSE OF THE TEST |
| COMPRESS 200mm U -SHAPED FIBER PROTECTOR 20mm/MINUTE UNTIL IT BREAKS. THE RESULT ON THE TABLE IS WEIGHT OF BREAKING POINT. |
TO GET BEND-BREAKING LOAD WEIGHT. |
|
|
| RESULTS | These tests were performed by IS-10T and RS-2 made by Shimazu Co., Ltd
at Chibaken Mechanical-Metal Examination Institute and Tokyo-Metropolitan-Mechanical-Technology
Center on 08/28/1989. Observer: Shimizu, Hagitec Co., Ltd. *Remarks* These datas are only for reference for the products. |
|||
| TYPE | Range/kg | BREAKING COMPRESSION/kg | BEGINS TO BEND AT | |
| KS-5N | 100 | 43 | 35Kg | |
| KS-9N | 100 | 65 | 40Kg | |
| KS-13N | 100 | 74 | 48Kg | |
| SX-5N | 200 | 80 | 56Kg | |
| IS-9N | 200 | 90 | 65Kg | |